Electrozi inveliti pentru sudare MMA - aliaje pe baza de nichel
| Tip electrod | Standard de clasificare | Compozitie Chimica % |
Caracteristici mecanice | Dimensiune | ||
| OK 92.05 Vac Pac |
AFA/AWS A5.11-ENi-1 DIN 1736-EL-NiTi3 |
C Si Mn Fe Ti Ni |
0,05 1,0 0,7 0,7 3,0 92,0 |
Forta alungire Forta rupere Alungire |
320 MPa 450 MPa 25 % |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||
| OK 92.15 | SFA/AWS A5.11-ENiCrFe-2 DIN 1736-EL-NiCr15FeNb |
C Si Mn Cr Ni Mo Nb Fe |
0,1 0,5 2,0 15,5 70,0 2,0 2,0 8,0 |
Forta alungire Forta rupere Alungire Rezilienta +20°C Rezilienta -196°C |
420 MPa 660 MPa 45 % 110 J 90J |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||
| OK 92.15 Vac Pac |
SFA/AWS A5.11-ENiCrFe-3 DIN 1736-EL-NiCr15FeMn |
C Si Mn Cr Ni Nb Fe |
0,1 0,6 6,0 16,0 70,0 2,0 6,0 |
Forta alungire Forta rupere Alungire Rezilienta +20°C Rezilienta -196°C |
410 MPa 640 MPa 40 % 100 J 80 J |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||
| Φ 5,0 x 350 | ||||||
| OK 92.26 | SFA/AWS A5.11 - ENiCRFe-3 EN ISO 14172 - E Ni 6182 |
C Si Mn Cr Ni Nb Cu Ti Ta Fe |
0,03 0,5 6,6 15,8 67 1,1 0,5 0,5 0,3 8,8 |
Forta alungire Forta rupere Alungire Rezilienta +20°C Rezilienta -196°C |
410 MPa 640 MPa 40 % 100 J 80 J |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||
| Φ 5,0 x 350 | ||||||
| OK 92.35 Vac Pac |
SFA/AWS A5.11-90-ENiCrMo-5 DIN 8555-E23-E250 CKT |
C Si Mn Mo Cr W Fe Ni |
0,06 0,7 0,7 16,5 15,5 3,8 5,5 57,0 |
Forta alungire Forta rupere Alungire |
515 MPa 750 MPa 17 % |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||
| Φ 5,0 x 350 | ||||||
| OK 92.45 Vac Pac |
SFA/AWS A5.11-ENiCrMo-3 DIN 1736-EL-NiCr20Mo9Nb |
C Si Mn Cr Ni Mo Nb Fe |
0,03 0,4 0,4 22,0 64,0 9,5 3,3 3,0 |
Forta alungire Forta rupere Alungire Rezilienta +20°C Rezilienta -196°C |
480 MPa 800 MPa 40 % 70 J 50 J |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||
| OK 92.55 | SFA/AWS A5.11-ENiCrMo6 | C Si Mn Cr Ni Mo Nb W Fe |
0,08 0,7 3,0 13,0 70,0 6,5 1,3 1,5 4,0 |
Forta alungire Forta rupere Alungire Rezilienta +20°C Rezilienta -60°C Rezilienta -196°C |
460 MPa 705 MPa 40 % 95 J 90 J 80 J |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||
| OK 92.59 | DIN 1726-EL-NiCr22Mo16 | C Si Mn Cr Ni Mo |
0,02 0,1 0,15 15,0 Bal 23,0 |
Forta alungire Forta rupere Alungire Rezilienta -60°C Rezilienta -196°C |
430 MPa 770 MPa 40 % 70 J 60 J |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||
| OK 92.82 | EN ISO 14172 - E Ni 6082 | C Si Mn Cr Ni Mo Nb Cu Ti Fe |
0,03 0,4 4,8 19,4 67 1,0 2,3 0,5 0,5 2,3 |
Forta alungire Forta rupere Alungire Rezilienta +20°C Rezilienta -196°C |
390 MPa 620 MPa 35 % 80 J 65 J |
Φ 2,5 x 300 |
| Φ 3,2 x 300 | ||||||
| Φ 4,0 x 350 | ||||||
| OK 92.86 | SFA/AWS A5.11 - E NiCu-7 EN ISO 14172 - E Ni 4060 |
C Si Mn Ni Nb Cu Al Ti Fe |
0,01 0,3 2,1 66 0,3 29 0,5 0,2 1,6 |
Forta alungire Forta rupere Alungire Rezilienta +20°C Rezilienta -196°C |
410 MPa 640 MPa 40 % 100 J 80 J |
Φ 2,5 x 300 |
| Φ 3,2 x 350 | ||||||
| Φ 4,0 x 350 | ||||||